PA-CF
Carbon-Fiber Reinforced Polyamide (PA6-CF)
Nylon (PA6) reinforced with 20% chopped carbon fibers. Delivers high mechanical stiffness, high strength-to-weight ratio, and thermal stability.
MECHANICAL RATING
Manufacture in PA-CF
Submit your CAD file (STEP, STL, or 3MF) for immediate slicing orientation, infill calculation, and an itemized engineering quote.
REQUEST A QUOTE WITH THIS MATERIAL →Mechanical & Physical Specifications
| Property Metric | Manufacturer Datasheet Value | Test Method |
|---|---|---|
| Tensile Strength | 105 MPa | ISO 527 |
| Flexural Modulus | 7.2 GPa | ISO 178 |
| Heat Deflection Temperature (HDT) | 150°C (0.45 MPa) | ISO 75 |
| Impact Resistance | 12 kJ/m² | ISO 179 / Charpy |
| Density | 1.18 g/cm³ | ISO 1183 |
| Elongation at Break | 4.5% | ISO 527 |
* Values represent nominal metrics published in raw filament manufacturer technical datasheets (tested on standard ISO/ASTM test specimens). Real-world 3D printed part performance is anisotropic and depends on build orientation, perimeter wall count, and infill geometry.
Chemical & Environmental Profile
High resistance to engine oils, gasoline, lubricants, and organic industrial solvents.
Recommended Applications
Robotics chassis, structural drone components, motor brackets, aluminum replacement parts, high-stiffness tooling fixtures.
Manufacturing & Slicing Parameters
Switch to Another Engineering Material
Browse full mechanical datasheets across all 9 standard polymers and composites.